What Is 5052 H32 Aluminum?
5052-H32 aluminum has a temper of H32. This means it has been strain hardened to a 1/4 hard temper and thermally stabilized. Aluminum alloy 5052 in H32 temper has very good corrosion resistance to seawater and marine, atmosphere.
It is a medium to high strength alloy and a medium to high fatigue strength. Its strength is slightly higher than 5251
It also has very good weldability and good cold formability.
5052 H32 Aluminum Alloy Chemical Element Content %
- Manganese (Mn): 0.0 – 0.10
- Iron (Fe) :0.0 – 0.40
- Copper (Cu): 0.0 – 0.10
- Magnesium (Mg) :2.20 – 2.80
- Silicon (Si) :0.0 – 0.25
- Zinc (Zn): 0.0 – 0.10
- Chromium (Cr) :0.15 – 0.35
- Others (Total): 0.0 – 0.15
- Other (Each): 0.0 – 0.05
- Aluminium (Al) :Balance
5052 H32 Aluminum Properties
| Physical Properties | |
| Density | 2.68 g/cc |
| Mechanical Properties | |
| Hardness, Brinell | 60 |
| Hardness, Knoop | 83 |
| Hardness, Vickers | 68 |
| Tensile Strength, Ultimate | 228 MPa |
| Tensile Strength, Yield | 193 MPa |
| Elongation at Break | 12 % @Thickness 1.59 mm |
| 18 % @Diameter 12.7 mm | |
| Modulus of Elasticity | 70.3 GPa |
| Poissons Ratio | 0.33 |
| Fatigue Strength | 117 MPa @# of Cycles 5.00e+8 |
| Shear Modulus | 25.9 GPa |
| Shear Strength | 138 MPa |
| Electrical Properties | Metric |
| Electrical Resistivity | 0.00000499 ohm-cm @Temperature 20.0 °C |
| Thermal Properties | Metric |
| Specific Heat Capacity | 0.880 J/g-°C |
| Thermal Conductivity | 138 W/m-K |
| Melting Point | 607.2 – 649 °C |
| Solidus | 607.2 °C |
| Liquidus | 649 °C |
| Processing Properties | Metric |
| Annealing Temperature | 343 °C |
| Hot-Working Temperature | 260 – 510 °C |
Characteristics
Very good corrosion resistance to seawater and marine and industrial atmosphere
Very good weldability and good cold formability
Decorative finish
Hard wearing
Non-slip
Corrosion resistant
Low maintenance
Anti-Static
Lightweight
Applications
Treadplate
Boilermaking
Containers
Nameplates
Road Signs
Architectural Panelling
Welded Tubes
Chemical Industry
Irrigation
Desalination units
Pressure Vessels
Rivets
Aluminum 5052 H32 Forms
5052-H32 Sheet 5052-H32 Plate, Extrusions
5052 H32 Aluminum What is used for
- Marine Applications
- Architecture
- Home & Office
- Transportation
- Manufacturing
5052 H32 Aluminum Price
Welcome send inquiry to us: info@jcmetalchina.com
5052 H32 Aluminum Supplier
JC Metal is a 5052-H32 Aluminum supplier. We are your source with competitively priced raw materials. Our order is no MOQ. Speed delivery worldwide. We provide you with best-in-class service on each order.
Logo in www.jcmetalchina.com or email us: info@jcmetalchina.com to inquiry: AA5052-H32; Al5052-H32
RFQCan you bend 5052-H32 aluminum?What is the difference between 5052 H32 and 5052 H34?Can 5052 H32 be annealed?
Alloy 5052 is not hardenable by heat treatment. So 5052 H32 can not be annealed.
To soften Alloy 5052 it can be annealed by heating to 345°C. hold until uniform temperature then cool. the rate of cooling is not important.