Description

2A14 aluminum sheets are characterized by high hardness and hard aluminum alloy. Among them, the content of copper is the highest, about 3-5%. Has good machinability. Resistivity. Good spot welding and seam welding performance. Can be strengthened by heat treatment. There is a squeezing effect. Thus, the vertical and horizontal performance are different. The tensile strength of 2A14 aluminum plate can reach 420MPa. The elongation is more than 10%.

JC Metal China is a 2000 Series Aluminum Sheet Supplier. The main type is 2014,2017,2024,2A11,2A12,2A14 aluminum sheet.

2A14 series aluminum plates are aviation aluminum materials. It is rarely used in conventional industries at present.

2A14 Aluminum Sheet Chemical Composition

Si	Cu	Mg	Zn	Mn	Ti	Fe	Ni
0.6-1.2	3.9-4.8	0.4-0.8	≤0.3	0.40-1.0	≤0.15	0.00-0.7	≤0.1

2024 aluminum plate characteristics

1. The elongation of 2A14 aluminum plate is over 10% , the hardness can reach 135HB, and the natural aging can reach 15h.

2,2A14 aluminum plate has good machinability, its resistivity, spot welding and seam welding performance is also very good.

3,2A14 aluminum plate with 2A11 aluminum plate, is a hard aluminum alloy, high strength, good thermal conductivity, can do heat treatment.

Uses

2A14 is used for applications requiring high strength and hardness (including high temperatures) , such as aircraft heavy, forgings, heavy plates and extruded materials, wheels and structural elements, first stage fuel tanks for multistage rockets and spacecraft parts, parts of truck frame and suspension system.

2A14 aluminum plate Mechanical Properties

Tensile strength σb (MPa)	≥440
Elongation δ5(%)	≥10

Sample size: bar diameter (diameter of inscribed circle of square bar and hexagon bar)≤22

Note: longitudinal mechanical properties of tubes at room temperature

2A14 aluminum plate Heat Treatment

Homogenization annealing

Heating 475 ~ 490 °C; Heat Preservation 12 ~ 14h; furnace cooling.

Complete Annealing

Heating 350 ~ 400 °C, holding time 30 ~ 120 min according to material thickness, air cooling after furnace temperature dropping below 300 °C/H at 30 ~ 50 °C.

Rapid annealing

Heating 350 ~ 460 °C; holding time 30 ~ 120 min; air cooling.

Quenching and aging

Quenching at 495 ~ 505 °C, water cooling and natural aging at room temperature for 96 H.

2A14 aluminum plate Price

1. JC Metal China 2A14 Aluminum Sheet price = Ingot Cost/Raw aluminum cost + Processing cost.
2. 2A14 Aluminum Sheet unit price is $/ton,$/kg,$/Pound,$/lbs.
3. 2A14 Aluminum Sheet price will be different as per the below factors. Such as Length, Width, Thickness, State, Surfaces Treatment.
4. Business Term: FOB,CFR,CIF,DDP,DUP…
5. Payment Term: TT.LC.TT+LC…

Packing

1–Install wooden pallets. Use steel belts to reinforce them to avoid collisions during transportation.
2–Can be packed as per customer’s requirements.

2A14 aluminium plate Technical Parameters

Material State	F、T4、T6、T351、O
Thickness	1mm-600mm
Width	500mm-2650mm
Length	500mm-16000mm

Market Applications

2A14 is used for applications requiring high strength and hardness (including high temperatures). Such as plane heavy, forgings, heavy plates, extruded materials. Wheels and structural elements. First stage fuel tanks for multistage rockets and spacecraft parts. Truck frame and suspension system.